FuturaJet universal powder

Monomer liquid for your FuturaJet acrylic. FuturaJet is the multi-talent in the acrylics world. It is eminently suitable for the injection method and all conventional acrylics techniques. Your benefits: Wide choice of colors Easy to use Universally applicable Excellent mechanical properties Extraordinary fit Polymerization: Flask temperature 35 °C (95 °F), injection pressure 30 min. Polymerization time: 15 min. at 2-4 bar, water temperature 45 °C (113 °F). Mixing ratio powder:liquid (weight [g]): 2:1 (free dosage) Processing time: 4.5 min. Physical properties: Vickers hardness: ca. 140 MPa Flexural strength: ca. 95 MPa E-module: ca. 2,700 MPa Water absorption: 23.3 µg/mm³ Water solubility: 1.1 µg/mm³ Residual monomer: complies with the standard Availability of FuturaJet powder: 500 g or 1 kg container.  

Polishing paste for all metals including titanium.

All-in-one. Multitalent. Neue verbesserte Formel. Universell einsetzbar. Ihre Vorteile: Jetzt noch schnellere Ausarbeitung und Politur für Top-Ergebnisse Breites Indikationsspektrum Noch universeller einsetzbar Noch einfacher in der Anwendung Noch bessere Passung Sicherere Verarbeitung: Hohe Fehlertoleranz Große Farbauswahl: 8 Farben: rosa, rosa-opak, rosa-geadert, rosa-transparent, rosa-transparent-geadert, rosa C, rosa K, klar Indikationen: All-in-one: Hervorragend geeignet für alle herkömmlichen Kunststofftechniken. Injektionsverfahren Reparaturen Modellgusskomplettierungen Totalprothesen Unterfütterungen Schienen

Tizian Blank PMMA Splint is made of a highly pure themoplastic PMMA which is produced following the highest quality standards. The crystal clear, color-stable material stands out with its homogeneity, low plaque adhesion and low water absorption. Tizian Blank PMMA Splint is an economic alternative for the splint technology. It can be be repaired and extended with PMMA acrylics. Indications: Occlusion splints Drilling templates for navigated implantation Lost wax technique in casting technology Processing: Due to the chemical and physical properties of thermoplastic PMMA, there is a risk of melting the material during dry machining and thus smearing the mills. Therefore, it is important to use only single-edged mills. If necessary, the milling strategy must be adjusted with a slower cutting speed and a lower feed rate. The material can be processed by wet machining with PMMA mills in a standard strategy without restrictions. 

Tizian Blank PMMA Splint is made of a highly pure themoplastic PMMA which is produced following the highest quality standards. The crystal clear, color-stable material stands out with its homogeneity, low plaque adhesion and low water absorption. Tizian Blank PMMA Splint is an economic alternative for the splint technology. It can be be repaired and extended with PMMA acrylics. Indications: Occlusion splints Drilling templates for navigated implantation Lost wax technique in casting technology Processing: Due to the chemical and physical properties of thermoplastic PMMA, there is a risk of melting the material during dry machining and thus smearing the mills. Therefore, it is important to use only single-edged mills. If necessary, the milling strategy must be adjusted with a slower cutting speed and a lower feed rate. The material can be processed by wet machining with PMMA mills in a standard strategy without restrictions.