priti®perfect transpa-blue,

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

priti® perfectKeep it simple! priti®perfect stands for: Stability of the color effect from the model to the mouth. It is easy to keep control with brush technique and the pasty masses. The final color shows already during application. priti®perfect aims at the single firing solution with only 20 components. Nevertheless, depending on the case, the double firing solution or internal staining is also an option. The perfect finish pritidenta is at your side with intelligent solutions from determining the shade to the insertion of the restoration. Mill teeth from multicolor material, sinter them and finalizing them aesthetically! This is simple, fast, first-class and therefore already masterful! priti®perfect gives the existing priti® concept the very last finishing touch. This is sophisticated perfection for aesthetics! Your benefits: Highly aesthetic colors, with only 20 components - final colors already visible during application Effective design: single firing solution preferred Released for: Zirconium dioxide Monolithic zirconium dioxide Layered ceramics for zirconium dioxide Layered ceramics for metals Lithium disilicate

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

priti® perfectKeep it simple! priti®perfect stands for: Stability of the color effect from the model to the mouth. It is easy to keep control with brush technique and the pasty masses. The final color shows already during application. priti®perfect aims at the single firing solution with only 20 components. Nevertheless, depending on the case, the double firing solution or internal staining is also an option. The perfect finish pritidenta is at your side with intelligent solutions from determining the shade to the insertion of the restoration. Mill teeth from multicolor material, sinter them and finalizing them aesthetically! This is simple, fast, first-class and therefore already masterful! priti®perfect gives the existing priti® concept the very last finishing touch. This is sophisticated perfection for aesthetics! Your benefits: Highly aesthetic colors, with only 20 components - final colors already visible during application Effective design: single firing solution preferred Released for: Zirconium dioxide Monolithic zirconium dioxide Layered ceramics for zirconium dioxide Layered ceramics for metals Lithium disilicate