priti®multidisc ZrO2 multicolor Extra Translucent, 98 x 25, Color A dark

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

Diamond radius cutter, double-edged, edge Ø 1 mm, shaft Ø 3 mm, total length 48 mm. Max. blank height = 25 mm. Processing type: fine finishing Blank material: zirconium Type: diamond polished Coding color: gold For the milling machines: Tizian Cut 5 without optional metal milling (3 mm shaft)

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

Used for the fabrication of temporary crowns and bridges to replace teeth or groups of teeth. Use in all open CAD-CAM systems   Your benefits: Very high material homogeneity due to the industrial polymerization process. Balanced combination of breaking strength and elasticity for clinical use. This guarantees excellent long-term stability. Excellent abrasion resistance. Ensures high process reliability, no mixing errors, no polymerization shrinkage and no unpleasant odour, as no hand mixing or cartridge. Extended milling properties thanks to economical production. Long-lasting color stability and aesthetics. Natural fluorescence.