Tizian Blank MT + 98 mm

"with graduated light transmission translucence of 49 % to 45 % Special features:Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body. Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible. The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide. Graduated strength The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications. Material Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength: typical mean value ? 1,100 MPa Translucence graduation of <

"with graduated light transmission translucence of 49 % to 45 % Special features:Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body. Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible. The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide. Graduated strength The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications. Material Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength: typical mean value ? 1,100 MPa Translucence graduation of <

"with graduated light transmission translucence of 49 % to 45 % Special features:Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body. Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible. The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide. Graduated strength The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications. Material Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength: typical mean value ? 1,100 MPa Translucence graduation of <

Available in 16 VITA shades and in white, with a translucency of 40 %.Indications:   Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks     Highly recommended for partially or fully veneered aesthetic work Advantages of monochromatic precolored blanks Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product. Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results. Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material:   Zirconium type II, class 5 according to DIN EN ISO 6872   Good flexural strength of >, 1,100 MPa   High translucency of 40 % High aesthetics   Very good resistance to aging   Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm   Biocompatible    

"with graduated light transmission translucence of 49 % to 45 % Special features:Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body. Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible. The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide. Graduated strength The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications. Material Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength: typical mean value ? 1,100 MPa Translucence graduation of <

"with graduated light transmission translucence of 49 % to 45 % Special features:Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body. Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible. The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide. Graduated strength The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications. Material Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength: typical mean value ? 1,100 MPa Translucence graduation of <